Resin-SZUV-S9006-tenacity dhuwur
Pambuka 3D Printing Materials
Karakteristik
SZUV-S9006?
DESKRIPSI PRODUK
SZUV-S9006 punika ABS kaya SL resin kang wisdhuwur-kateguhanfitur. Iki dirancang kanggo printer SLA solid state. SZUV-S9006 bisa diterapake ing pola master, model konsep, bagean perakitan lan prototipe fungsional ing bidang industri otomotif, medis lan elektronik konsumen. Bangunan kekiatan bagean kanthi SZUV-S9006 luwih saka 6.5 wulan.
?
TIPIKALFITUR
-Liquid resin kang medium viskositas, supaya gampang recoating, gampang kanggo ngresiki bagean lan mesin
-Kekuwatan sing luwih apik ditahan, retensi dimensi sing luwih apik saka bagean ing kondisi lembab
-perlu finishing bagean minimal
- Urip beting dawa ing mesin
-kurangkontraksi ngisor?
?
TIPIKALPAEDAHE
-Mbutuhake wektu rampung sing luwih sithik, luwih gampang sawise ngobati
-Bulid akurat lan dhuwur bagean angel karo stabilitas dimensi apik
-Kontrol kualitas dhuwur kanggo bagean casting vakum
- Nyilikake kurang lan resistance apik kanggo yellowing
- Werna putih sing apik banget
-Material SLA machinable pinunjul?
Cathetan: suhu szuv-s9006 ngirim ora dhuwur banget. Mangga gunakake ing ngisor 25 ℃. Kelembapan relatif kanggo panggunaan lan panyimpenan kudu kurang saka 38RH%.
?
Kasus Aplikasi
Sawetara PROYEK MY
Pendidikan
Cetakan Tangan
Auto Parts
Desain Kemasan
Seni Desain
medis
?
?Sifat Fisik (Cairan)
| Penampilan | Putih |
| Kapadhetan | 1.11-~1.15g/cm3@ 25 ℃ |
| Viskositas | 230~290cps @ 26 ℃ |
| Dp | 0,13 ~ 0,145 mm |
| Ec | 9,5 ~ 10,5 mJ/cm2 |
| Ketebalan lapisan bangunan | 0,05 ~ 0,12 mm |
?
Sifat Mekanik (Post-Cured)
| PENGUKURAN? | METODE UJI? | NILAI |
| 90-menit UV pasca-tamba | ||
| Hardness, Shore D | ASTM D 2240 | 75-85 |
| Modulus lentur, Mpa | ASTM D 790 | 2.592-2.675 |
| Kekuatan lentur, Mpa | ASTM D 790 | 63-70 |
| Modulus tarik, MPa | ASTM D 638 | 2.489-2.595 |
| Kekuatan tarik, MPa | ASTM D 638 | 36-53 |
| Elongation ing break | ASTM D 638 | 15-25% |
| Rasio Poisson | ASTM D 638 | 0.4-0.44 |
| Kekuwatan impact notched Izod, J/m | ASTM D 256 | 45-70 |
| Suhu defleksi panas, ℃ | ASTM D 648 @66PSI | 38-50 |
| Transisi kaca, Tg | DMA, E "puncak | 40-54 |
| Koefisien biaya termal | TMA (T | 90~102*E-6 |
| Kapadhetan, g / cm3 | ? | 1.12-1.18 |
| Konstanta dielektrik 60 Hz | ASTM D 150-98 | 4.2-5.0 |
| Konstanta dielektrik 1 kHz | ASTM D 150-98 | 3.3-4.2 |
| Konstanta dielektrik 1 MHz | ASTM D 150-98 | 3.2-4.0 |
| Kekuwatan DielektrikkV/mm | ASTM D 1549-97a | 12.8-16.1 |
?